@misc{Hwang_Kyu-Seog_Red-emitting_2009, author={Hwang, Kyu-Seog and Jeon, Young-Sun and Hwangbo, Seung and Kim, Jin-Tae}, contributor={Gaj, Miron. Redakcja and Urbańczyk, Wacław. Redakcja}, year={2009}, rights={Wszystkie prawa zastrzeżone (Copyright)}, description={Optica Applicata, Vol. 39, 2009, nr 2, s. 375-382}, publisher={Oficyna Wydawnicza Politechniki Wrocławskiej}, language={eng}, abstract={Scheelite-type LiEuW2O8 (LEW) phosphors with the optical function of color conversion from near-UV to red were prepared by sol–gel method using a lithium acetate dehydrate, europium(III) nitrate pentahydrate, and tungsten(VI) chloride as starting materials. Viscous mixing sol was prefired at 300 °C for 120 min in air and then white powder precursor was finally annealed at 500–800 °C for 240 min in Ar. From an X-ray diffraction analysis, all the samples are isostructural and belong to the tetragonal system of scheelite-type. The main emission peak is 5D0 → 7F2 transitions of Eu3+ at 615 nm, other transitions from the 5D0 → 7F1, 5D0 → 7F3 and 5D0 → 7F4 located at 570–700 nm range are weak. The characteristic emission of WO4–2 in LEW is quenched absolutely and only red-light emission of Eu3+ appears. Crystallinity, surface properties and red-emission by near-ultraviolet (395 nm) were improved by high-temperature annealing.}, title={Red-emitting LiEuW2O8 phosphor for white emitting diodes prepared by sol–gel process}, type={artykuł}, keywords={optyka, phosphors, sol–gel, near-UV, red-light emission}, }