@misc{Hwang_Kyu-Seog_Chemical_2010,
 author={Hwang, Kyu-Seog and Hwangbo, Seung and Kim, Jin-Tae},
 contributor={Gaj, Miron. Redakcja and Urbańczyk, Wacław. Redakcja},
 year={2010},
 rights={Wszystkie prawa zastrzeżone (Copyright)},
 publisher={Oficyna Wydawnicza Politechniki Wrocławskiej},
 description={Optica Applicata, Vol. 40, 2010, nr 4, s. 943-948},
 language={eng},
 abstract={Eu2+-doped SrMg2(PO4)2 phosphor with blue emission was prepared by the low temperature chemical solution process using inorganic salts as a starting material. Transparent sol was preheated at 300 °C for 120 min and then precursor was finally annealed at 900 °C for 240 min in a reducing CO atmosphere. Crystallinity, surface morphology and luminescent properties have been investigated. The phosphor emits bright blue luminescence with a peak wavelength at 423 nm under near-ultraviolet excitation at 363 nm.},
 type={artykuł},
 title={Chemical solution-derived SrMg2(PO4)2:Eu2+ blue phosphor for ultraviolet emitting diodes},
 keywords={optyka, SrMg2(PO4)2, phosphor, blue, sol–gel},
}